安钢6号高炉长期休风及复风操作实践A


1 安钢6号高炉长期休风及复风操作实践 张晓亮 牛卫军 田黎明 张海洲
安阳钢铁集团有限责任公司 摘要 安钢6号高炉长期休风33.5小时计划检修送风后近9个小时恢复正常生产整个过程避免了风 口烧坏事故。本文对这次休复风操作进行了总结并分析了全开风口送风等恢复炉况的方法。 关键词 高炉 长期休风 复风 操作 Operation practice of long term blowing-down and
reblowing on Anyang Steel’s No.6 BF Zhang Xiaoliang Niu Weijun Tian Liming Zhang Haizhou
(Anyang Iron & Steel Group Co.,Ltd)
Abstract Long term blowing-down for 33.5 hours was carried out because of plan overhaul at
Anyang Steel’s No.6 BF,after reblowing it took nearly 9 hours to achieve the BF normal condition,
the operation had avoided the burn-out of tuyere accident in the entire process.This essay
summarizes the blowing-down and reblowing operation, analyzes the methods of resuming BF
condition ,such as reblowing with opening all tuyeres and so on. Key words BF long term blowing-down reblowing operation 1 概述
安钢6号高炉380m3设计1个渣口1个铁口14个风口液压双钟炉顶1999年元月22日建成投产取消了放上渣操作截止到2006年5月单位炉容产铁9092.60 t/m3已经进入炉役后期设备问题较多一般每隔2个多月就须一次设备检修。2006年6月22
日05:10至23日14:40高炉按照集团公司统一安排长期休风33.5小时计划检修送风后
近9个小时恢复正常生产整个过程避免了风口烧坏事故。为了总结经验稳定高炉生产
本文总结了这次长期休风及复风操作实践并对此进行了技术分析。
2 休风前的高炉状况
6号高炉在2006年5月炉况整体上稳定顺行全月平均利用系3.71t/(m3?d)煤比152
kg/t焦比387 kg/t[Si]为0.54%风温1030℃。高炉冷却壁仅在炉身下部有三块漏水已
经全部灌浆闷死采取炉外喷水冷却高炉炉底温度偏高小钟破损严重炉前水冷撇渣器
需要及时修补。高炉采用高碱度烧结矿+球团+块矿炉料结构富氧使用炼钢余氧。
3休复风操作原则
1针对炼铁厂同期检修的还有其它3座高炉其中个别高炉检修送风后顺行不好
这次休风要确保高炉送风后炉况顺行不能再影响供给炼钢铁水。
2复风时堵远离铁口位置的部分风口或风口临时加砖套临时缩小风口面积低风
压时提高鼓风速度加到一定程度风压打开视孔盖用钢钎捅掉砖套恢复原来风口面积
保证刚送风有一定的风速。掌握好捅开风口的时机争取杜绝烧风口现象。
3高炉在炉役后期要考虑漏水等因素有防凉措施送风后控制好炉温和碱度
尽量减轻炉前

第1页

TOP相关主题

  • 高炉休风
  • 顾仲安钢笔行书字帖
  • 安钢论坛
  • 安钢集团
  • 安钢微博
  • 安钢贴吧
  • 安阳论坛 安钢社区
  • 保定警察安钢

我要评论

相关文档

站点地图 | 文档上传 | 侵权投诉 | 手机版
新浪认证  诚信网站  绿色网站  可信网站   非经营性网站备案
本站所有资源均来自互联网,本站只负责收集和整理,均不承担任何法律责任,如有侵权等其它行为请联系我们.
文档下载 Copyright 2013 doc.xuehai.net All Rights Reserved.  email
返回顶部